Liquid crystalline medium and liquid crystal display

ABSTRACT

The instant invention relates to dielectrically positive liquid crystalline media comprising a dielectrically positive component, component A, comprising a dielectrically positive compound of formula I 
                         
wherein the parameters have the meaning given in the specification, and optionally a second dielectrically positive component, component B, comprising one or more dielectrically positive compounds having a dielectric anisotropy of more than 3 and optionally a dielectric neutral component, component C, as well as to liquid crystal displays comprising these media, especially to active matrix displays and in particular to TN and to IPS displays.

FIELD OF THE INVENTION

The present invention relates to liquid crystalline media and to liquid crystal displays comprising these media, especially to displays addressed by an active matrix and in particular to displays of the Twisted Nematic (TN) or of the In Plane Switching (IPS) type.

STATE OF THE ART AND PROBLEM TO BE SOLVED

Liquid Crystal Displays (LCDs) are widely used to display information. LCDs are used for direct view displays, as well as for projection type displays. Electro-optical modes employed are, e.g., the twisted nematic (TN)-, the super twisted nematic (STN)-, the optically compensated bend (OCB)- and the electrically controlled birefringence (ECB)-mode with their various modifications, as well as others. All these modes use an electrical field, which is substantially perpendicular to the substrates, respectively to the liquid crystal layer. Besides these modes there are also electro-optical modes employing an electrical field substantially parallel to the substrates, respectively the liquid crystal layer, like, e.g., the In-Plane Switching mode (as disclosed, e.g., in DE 40 00 451 and EP 0 588 568). Especially this electro-optical mode is used for LCDs for modern desktop monitors and is envisaged to be applied for displays for multi media applications. The liquid crystals according to the present invention are preferably used in this type of displays.

For these displays new liquid crystalline media with improved properties are required. Especially the response times have to be improved for many types of applications. Thus liquid crystalline media with lower viscosities (η), especially with lower rotational viscosities (γ₁) are required. The rotational viscosity should be 75 mPa·s or less, preferably 60 mPa·s or less and especially 55 mPa·s or less. Besides this parameter, the media have to exhibit a suitably wide range of the nematic phase, an appropriate birefringence (Δn) and dielectric anisotropy (Δ∈) should be high enough to allow a reasonably low operation voltage. Preferably, Δ∈ should be higher than 4 and very preferably higher than 5, preferably, however, not higher than 15 and in particular not higher than 12, as this would be detrimental for an at least reasonably high specific resistivity.

The displays according to the present invention are preferably addressed by an active matrix (active matrix LCDs, short AMDs), preferably by a matrix of thin film transistors (TFTs). However, the inventive liquid crystals can also beneficially be used in displays with other known addressing means.

There are various different display modes using composite systems of liquid crystal materials of low molecular weight together with polymeric materials. These are, e.g., polymer dispersed liquid crystal (PDLC)-, nematic curvi-linearly aligned phase (NCAP)- and polymer network (PN)-systems, as disclosed for example in WO 91/05 029, or axially symmetric microdomain (ASM) systems and others. In contrast to these, the modes especially preferred according to the instant invention are using the liquid crystal medium as such, oriented on surfaces. These surfaces typically are pre-treated to achieve uniform alignment of the liquid crystal material. The display modes according to the instant invention preferably use an electrical field substantially parallel to the composite layer.

Liquid crystal compositions suitable for LCDs and especially for IPS displays are known, e.g., from JP 07-181 439 (A), EP 0 667 555, EP 0 673 986, DE 195 09 410, DE 195 28 106, DE 195 28 107, WO 96/23 851 and WO 96/28 521. These compositions, however, do have significant drawbacks. Most of them, amongst other deficiencies, lead to unfavourably long response times, have too low values of the resistivity and/or require operation voltages, which are too high.

The synthesis of compounds with a

moiety is described in the applications PCT/EP2006/004140 and PCT/EP2006/004425.

Thus, there is a significant need for liquid crystalline media with suitable properties for practical applications such as a wide nematic phase range, appropriate optical anisotropy Δn, according to the display mode used, a high Δ∈ and especially low viscosities.

PRESENT INVENTION

Surprisingly, it now has been found that liquid crystalline media with a suitably high Δ∈, a suitable phase range, and Δn can be realized, which do not exhibit the drawbacks of the materials of the prior art or at least do exhibit them to a significantly lesser degree.

These improved liquid crystalline media according to the instant application are comprising at least the following components:

-   -   a first dielectrically positive component, component A,         comprising one or more dielectrically positive compounds of         formula I

wherein

-   R¹ is alkyl, alkoxy, fluorinated alkyl or fluorinated alkoxy with 1     to 7 C-atoms, alkenyl, alkenyloxy, alkoxyalkyl or fluorinated     alkenyl with 2 to 7 C-atoms, and preferably are alkyl or alkenyl,

-    are independently of each other

-   X¹ is halogen, halogenated alkyl or alkoxy with 1 to 3 C-atoms or     halogenated alkenyl or alkenyloxy with 2 or 3 C-atoms, preferably F,     Cl, —OCF₃ or —CF₃, most preferably F, Cl or —OCF₃, and     -   optionally, a second dielectrically positive component,         component B, comprising one or more dielectrically positive         compounds, preferably having a dielectric anisotropy of more         than 3, preferably selected from the group of compounds of         formulae II and III

wherein

-   R² and R³, independently of each other, are alkyl, alkoxy,     fluorinated alkyl or fluorinated alkoxy with 1 to 7 C-atoms,     alkenyl, alkenyloxy, alkoxyalkyl or fluorinated alkenyl with 2 to 7     C-atoms, and R² and R³ preferably are alkyl or alkenyl,

-    are, independently of each other,

-   L²¹, L²², L³¹ and L³², are, independently of each other, H or F,     preferably L²¹ and/or L³¹ is F, -   X² and X³ are, independently of each other, halogen, halogenated     alkyl or alkoxy with 1 to 3 C-atoms or halogenated alkenyl or     alkenyloxy with 2 or 3 C-atoms, preferably F, Cl, —OCF₃ or —CF₃,     most preferably F, Cl or —OCF₃, -   Z³ is —CH₂CH₂—, —CF₂CF₂—, —COO—, trans- —CH═CH—, trans- —CF═CF—,     —CH₂O— or a single bond, preferably —CH₂CH₂—, —COO—, trans- —CH═CH—     or a single bond and most preferably —COO—, trans- —CH═CH— or a     single bond, and -   l, m, n and o are, independently of each other, 0 or 1 and -   from which compounds of formula I are excluded, and     -   optionally a dielectrically neutral component, component C,         comprising one or more dielectrically neutral compounds of         formula IV

wherein

-   R⁴¹, and R⁴², independently of each other have the meaning given for     R² under formula II above, preferably R⁴¹ is alkyl and R⁴² is alkyl     or alkoxy, or R⁴¹ is alkenyl and R⁴² is alkyl,

-    independently of each other, and in case

-    is present twice, also these, independently of each other, are

-    preferably at least one of

-   Z⁴¹ and Z⁴² are, independently of each other, and in case Z⁴¹ is     present twice, also these independently of each other, —CH₂CH₂—,     —COO—, trans- —CH═CH—, trans- —CF═CF—, —CH₂O—, —CF₂O—, —C≡C— or a     single bond, preferably at least one of them is a single bond, and -   p is 0, 1 or 2, preferably 0 or 1.

Preferably, component A, comprises, more preferably it consists predominantly of, even more preferably it consists essentially of, and most preferably it consists entirely of one or more dielectrically positive compounds of formula I, having a dielectric anisotropy of more than 3, which preferably are selected from the group of formulae I-1 to I-3, in particular from I-1 and I-3

wherein the parameters have the respective meanings given under formula I above and preferably X¹ is F.

Preferably, the concentration of the component A in the medium is in the range from 1% to 70%, more preferably from 2% to 40%, even more preferably from 4% to 20% and most preferably from 5% to 15%.

Preferably, the media according to the present invention comprise a second dielectrically positive component, component B. Preferably, this second dielectrically positive component, component B, comprises, more preferably it consists predominantly of, even more preferably it consists essentially of, and most preferably it consists entirely of dielectrically positive compounds having a dielectric anisotropy of more than 3.

Preferably, this component, component B, comprises, more preferably it consists predominantly of, even more preferably it consists essentially of, and most preferably it consists entirely of one or more dielectrically positive compounds having a dielectric anisotropy of more than 3, selected from the group of formulae II and III.

In a preferred embodiment of the present invention component B, comprises, more preferably it consists predominantly of, even more preferably it consists essentially of, and most preferably it consists entirely of one or more dielectrically positive compounds having a dielectric anisotropy of more than 3, selected from the group of compounds of formulae II-1 and II-2

wherein the parameters have the respective meanings given under formula II above and in Formula II-1 the parameters L²³ and L²⁴ are, independently of each other and of the other parameters, H or F.

Preferably, component B comprises compounds selected from the group of compounds of formulae II-1 and II-2, wherein L²¹ and L²² or L²³ and L²⁴ are both F

In a preferred embodiment component B comprises compounds selected from the group of compounds of formulae II-1 and II-2, wherein L²¹, L²², L²³ and L²⁴ all are F.

Preferably, component B comprises one or more compounds of formula II-1. Preferably, the compounds of formula II-1 are selected from the group of compounds of formulae II-1a to II-1e

wherein the parameters have the respective meanings given above.

Preferably, component B comprises compounds selected from the group of compounds of formulae II-1a to II-1e wherein L²¹ and L²² or L²³ and L²⁴ are both F

In a preferred embodiment component B comprises compounds selected from the group of compounds of formulae II-1a to II-1e, wherein L²¹, L²², L²³ and L²⁴ all are F.

Especially preferred compounds of formula II-1 are

wherein the R² has the meaning given above.

Preferably, Component B comprises one or more compounds of formula II-2. Preferably, the compound of formula II-2 are selected from the group of compounds of formulae II-2a to II-2d

wherein the parameters have the respective meanings given above and preferably L²¹ and L²² are both F and L²³ and L²⁴ are both H, or L²¹, L²², L²³ and L²⁴ are all F

Especially preferred compounds of formula II-2 are

wherein the R² has the meaning given above.

In a further preferred embodiment of the present invention component B, comprises, more preferably it consists predominantly of, even more preferably it consists essentially of, and most preferably it consists entirely of one or more dielectrically positive compounds having a dielectric anisotropy of more than 3, selected from the group of formulae III-1 and III-2

wherein the parameters have the respective meanings given under formula III above.

Preferably, component B comprises one or more compounds of formula III-1. Preferably, the compounds of formula III-1 are selected from the group of compounds of formulae III-1a and III-1b

wherein the parameters have the respective meanings given above and the parameters L³³ and L³⁴ are, independently of each other and of the other parameters, H or F.

Preferably, component B comprises one or more compounds of formula III-2. Preferably, the compounds of formula III-2 are selected from the group of compounds of formulae III-2a to III-2g

wherein the parameters L³³ and L³⁴, and L³⁵ and L³⁶ are, independently of each other and of the other parameters, H or F.

Preferably, component B comprises one or more compounds of formula III-1a, which preferably are selected from the group of compounds of formulae III-1a-1 to III-1a-6

wherein the R³ has the meaning given above.

Preferably, component B comprises one or more compounds of formula III-2a, which are preferably selected from the group of compounds of formulae III-2a-1 to III-2a-4

wherein the R³ has the meaning given above.

Preferably, component B comprises one or more compounds of formula III-2b, which are preferably selected from the group of compounds of formulae III-2b-1 to III-2b-5

wherein the R³ has the meaning given above.

Preferably, component B comprises one or more compounds selected from the group of compounds of formulae III-2c and III-2d, which are preferably selected from the group of compounds of formulae III-2c-1 and III-2d-1

wherein the R³ has the meaning given above.

Preferably, component B comprises one or more compounds of formula III-2e, which are preferably selected from the group of compounds of formulae III-2e-1 to III-2e-5

wherein the R³ has the meaning given above.

Preferably, component B comprises one or more compounds of formula III-2f, which are preferably selected from the group of compounds of formulae III-2f-1 to III-2f-5

wherein the R³ has the meaning given above.

Preferably, component B comprises one or more compounds of formula III-2g, which are preferably selected from the group of compounds of formulae III-2g-1 to III-2g-3

wherein the R³ has the meaning given above.

Alternatively or additionally to compounds of formulae III-1 and/or III-2 the media according to the present invention may comprise one or more compounds of formula III-3

wherein the parameters have the respective meanings given under formula III above, and preferably of formula III-3a

wherein the R³ has the meaning given above.

Preferably, the liquid crystalline media according to the present invention comprise a dielectrically neutral component, component C. This component has a dielectric anisotropy in the range from −1.5 to 3. Preferably, it comprises, preferably consists predominantly of, preferably consists essentially of, and especially preferably consists entirely of dielectrically neutral compounds, having a dielectric anisotropy in the range from −1.5 to 3. Preferably, this component comprises one or more, more preferably consists predominantly of, more preferably consists essentially of and especially preferably consists entirely of dielectrically neutral compounds, having a dielectric anisotropy in the range from −1.5 to 3, of formula IV.

Preferably, the dielectrically neutral component, component C, comprises one or more compounds selected from the group of compounds of formulae IV-1 to IV-5

wherein R⁴¹ and R⁴² have the respective meanings given under formula IV above. In formulae IV-1, IV-4 and IV-5, R⁴¹ preferably is alkyl or alkenyl, preferably alkenyl and R⁴² preferably is alkyl or alkenyl, preferably alkyl. In formula IV-2, R⁴¹ and R⁴² preferably are alkyl, and, in formula IV-3, R⁴¹ preferably is alkyl or alkenyl, preferably alkyl, and R⁴² preferably is alkyl or alkoxy, preferably alkoxy.

Preferably, the dielectrically neutral component, component C, comprises one or more compounds selected from the group of compounds of formulae IV-1, IV-3, IV-4 and IV-5, preferably one or more compounds of formula IV-1 and one or more compounds selected from the group of formulae IV-3 and IV-4, preferably one or more compounds each of formulae IV-1, IV-3 and IV-4 and most preferably one or more compounds each of formulae IV-1, IV-3, IV-4 and IV-5.

In a further preferred embodiment of the present invention, which may the same as the previous one or a different one, the liquid crystal mixtures according to the present invention comprise component C, comprising, preferably predominantly consisting of, preferably essentially consisting of, and most preferably entirely consisting of compounds of formula IV selected from the group of compounds of formulae IV-1 to IV-5, as shown above, and optionally of formulae IV-6 to IV-13

wherein

-   R⁴¹ and R⁴² are, independently of each other, alkyl, alkoxy,     fluorinated alkyl or fluorinated alkoxy with 1 to 7 C-atoms,     alkenyl, alkenyloxy, alkoxyalkyl or fluorinated alkenyl with 2 to 7     C-atoms and -   L⁴ is H or F.

Alternatively or additionally to compounds of formulae II and/or III the media according to the present invention may comprise one or more dielectrically positive compounds of formula V

wherein

-   R⁵ is alkyl, alkoxy, fluorinated alkyl or fluorinated alkoxy with 1     to 7 C-atoms, alkenyl, alkenyloxy, alkoxyalkyl or fluorinated     alkenyl with 2 to 7 C-atoms, and preferably is alkyl or alkenyl,

-    are, independently of each other,

-   L⁵¹ and L⁵², are, independently of each other, H or F, preferably     L⁵¹ is F and -   X⁵ is halogen, halogenated alkyl or alkoxy with 1 to 3 C-atoms or     halogenated alkenyl or alkenyloxy with 2 or 3 C-atoms, preferably F,     Cl, —OCF₃ or —CF₃, most preferably F, Cl or —OCF₃, -   Z⁵ is —CH₂CH₂—, —CF₂CF₂—, —COO—, trans- —CH═CH—, trans- —CF═CF— or     —CH₂O, preferably —CH₂CH₂—, —COO— or trans- —CH═CH— and most     preferably —COO— or —CH₂CH₂—, and -   q is 0 or 1.

Preferably, the media according to the present invention comprises one or more compounds of formula V, preferably selected from the group of compounds of formulae V-1 and V-2

wherein the parameters have the respective meanings given above and the parameters L⁵³ and L⁵⁴ are, independently of each other and of the other parameters, H or F and preferably Z⁵ is —CH₂—CH₂—.

Preferably, the compounds of formula V-1 are selected from the group of compounds of formulae V-1a and V-1b

wherein the R⁵ has the meaning given above.

Preferably, the compounds of formula V-2 are selected from the group of compounds of formulae V-2a to V-2d

wherein the R⁵ has the meaning given above.

Preferably, the liquid crystalline media according to the present invention comprise an additional dielectrically neutral component, component D. This component has a dielectric anisotropy in the range from −1.5 to 3. Preferably, it comprises, preferably consists predominantly of, preferably consists essentially of and especially preferably consists entirely of dielectrically neutral compounds, having a dielectric anisotropy in the range from −1.5 to 3. Preferably, this component comprises one or more, more preferably comprises predominantly of, more preferably comprises essentially of, and especially preferably consists entirely of dielectrically neutral compounds, having a dielectric anisotropy in the range from −1.5 to 3, of formula VI

wherein

-   R⁶¹, and R⁶², independently of each other have the meaning given for     R² under formula II above, preferably R⁶¹ is alkyl and R⁶² is alkyl     or alkenyl,

-    and in case it is occurring twice in each occurrence independently     of each other, is

-    preferably at least one of

-   Z⁶¹ and Z⁶² are, independently of each other, and in case Z⁶¹ is     present twice, also these independently of each other, —CH₂CH₂—,     —COO—, trans- —CH═CH—, trans- —CF═CF—, —CH₂O—, —CF₂O— or a single     bond, preferably at least one of them is a single bond, and -   r is 0, 1 or 2, preferably 0 or 1.

Preferably, the dielectrically neutral component, component D, comprises one or more compounds selected from the group of compounds of formulae VI-1 and VI-2

wherein R⁶¹ and R⁶² have the respective meanings given under formula VI above and R⁶¹ preferably is alkyl, and in formula VI-1 R⁶² preferably is alkenyl, preferably —(CH₂)₂—CH═CH—CH₃, and in formula VI-2 R⁶² preferably is alkyl.

Preferably, the dielectrically neutral component, component D, comprises one or more compounds selected from the group of compounds of formulae VI-1 and VI-2 wherein preferably R⁶¹ n-alkyl, and in formula VI-1 R⁶² preferably is alkenyl, and in formula VI-2 R⁶² preferably is n-alkyl.

Preferably, the liquid crystal mixtures according to the present invention do contain at least one further component besides components A and B. This third component may be either one of components C and D, preferably the third component present is component C.

Obviously the mixtures according to the present invention also can contain all four components A, B, C and D.

Additionally, the liquid crystal mixtures according to the present invention may comprise a further optional component, component E, which has a negative dielectric anisotropy and comprises, preferably predominantly consists of, more preferably essentially consists of, and most preferably entirely consists of dielectrically negative compounds preferably of formula VII

wherein

-   R⁷¹ and R⁷² independently of each other have the meaning given for     R² under formula II above,

-   Z⁷¹ and Z⁷² are, independently of each other, —CH₂CH₂—, —COO—,     trans- CH═CH—, trans- —CF═CF—, —CH₂O—, —CF₂O— or a single bond,     preferably at least one of them is a single bond and most preferably     both are a single bond, -   L⁷¹ and L⁷² are, independently of each other, C—F or N, preferably     at least one of them is C—F and most preferably both of them are C—F     and -   k is 0 or 1.

Preferably, the liquid crystalline media according to the instant invention comprise, more preferably predominantly consist of, more preferably essentially consist of, and most preferably entirely consist of components A to E, preferably A to D and most preferably A to C, and in particular of compounds selected from the group of compounds of formulae I to VII, preferably I to V and most preferably I to III.

Comprising in this application means in the context of compositions that the entity referred to, e.g. the medium or the component, contains the component or components or of the compound or compounds in question, preferably in a total concentration of 10% or more and most preferably of 20% or more.

Predominantly consisting of, in this context, means that the entity referred to contains 55% or more, preferably 60% or more and most preferably 70% or more of the component or components or of the compound or compounds in question.

Essentially consisting of, in this context, means that the entity referred to contains 80% or more, preferably 90% or more and most preferably 95% or more of the component or components or of the compound or compounds in question.

Entirely consisting of, in this context, means that the entity referred to contains 98% or more, preferably 99% or more and most preferably 100.0% of the component or components or of the compound or compounds in question.

Component E preferably comprises, preferably predominantly consists of, more preferably essentially consists of, and most preferably entirely consists of one or more compounds of formula VII, preferably selected from the group of compounds of formulae VII-1 to VII-3

wherein

-   R⁷¹ and R⁷² have the respective meanings given under formula VI     above.

In formulae VII-1 to VII-3 R⁷¹ preferably is n-alkyl or 1-E-alkenyl and R⁷² preferably is n-alkyl or alkoxy.

Also other mesogenic compounds, which are not explicitly mentioned above, can optionally and beneficially be used in the media according to the instant invention. Such compounds are known to the expert in the field.

The liquid crystal media according to the instant invention are characterized by a clearing point of 70° C. or more, preferably of 75° C. or more.

The Δn, at 589 nm (Na^(D)) and 20° C., of the liquid crystal media according to the instant invention preferably is in the range of 0.060 or more to 0.135 or less, more preferably in the range of 0.070 or more to 0.125 or less and most preferably in the range of 0.080 or more to 0.120 or less. Particularly preferred are media with Δn of 0.11 or less and preferably of 0.10 or less.

The Δ∈, at 1 kHz and 20° C., of the liquid crystal medium according to the invention preferably is 4.0 or more, more preferably 6.0 or more and most preferably 8.0 or more. In particular Δ∈ is 10.0 or more.

Preferably, the nematic phase of the inventive media extends at least from 0° C. or less to 70° C. more, more preferably at least from −20° C. or less to 70° C. more, most preferably at least from −30° C. or less to 75° C. more and in particular at least from −40° C. or less to 75° C. more.

In a first preferred embodiment of the present invention the Δn of the liquid crystal media is in the range of 0.090 or more to 0.125 or less, more preferably in the range of 0.095 or more to 0.120 or less and most preferably in the range of 0.100 or more to 0.115 or less, whereas Δ∈ preferably is in the range from 4.0 or more to 10.0 or less, preferably 7.0 or less.

In a second preferred embodiment of the present invention the Δn of the liquid crystal media is in the range of 0.085 or more to 0.130 or less, more preferably in the range of 0.090 or more to 0.125 or less and most preferably in the range of 0.095 or more to 0.120 or less, whereas Δ∈ preferably is 6.0 or more, more preferably 7.0 or more, even more preferably 8.0 or more and most preferably in the range from 8.0 or more to 10.0 or less.

In this embodiment preferably the nematic phase of the inventive media extends at least from −20° C. or less to 70° C. more, more preferably at least from −20° C. or less to 70° C. more, most preferably at least from −30° C. or less to 70° C. more and in particular at least from −40° C. or less to 70° C. more.

In a third preferred embodiment of the present invention the Δn of the liquid crystal media is in the range of 0.070 or more to 0.120 or less, more preferably in the range of 0.075 or more to 0.115 or less and most preferably in the range of 0.080 or more to 0.110 or less, whereas Δ∈ preferably is 4.0 or more, more preferably is in the range from 4.0 or more to 14.0 or less and most preferably either in the range from 4.0 or more to 6.0 or less or, particularly preferred in the range from 6.0 or more to 11.0 or less.

In this embodiment preferably the nematic phase of the inventive media extends at least from −20° C. or less to 70° C. or more, preferably to 75° C. more, more preferably at least from −30° C. or less to 70° C. more, most preferably at least from −30° C. or less to 75° C. more and in particular at least from −30° C. or less to 80° C. more.

In a fourth preferred embodiment of the present invention the Δn of the liquid crystal media is in the range of 0.080 or more to 0.150 or less, more preferably in the range of 0.085 or more to 0.145 or less and most preferably in the range of 0.090 or more to 0.140 or less, whereas Δ∈ preferably is 2.0 or more, more preferably is in the range from 2.0 or more to 14.0 or less and most preferably in the range from 3.0 or more to 12.0 or less.

In this embodiment preferably the nematic phase of the inventive media extends over the same preferred ranges as in the previous (i.e. the third preferred embodiment).

In a fifth preferred embodiment of the present invention the Δn of the liquid crystal media is in the range of 0.060 or more to 0.130 or less, more preferably in the range of 0.065 or more to 0.125 or less and most preferably in the range of 0.070 or more to 0.120 or less, whereas in this embodiment Δ∈ is in and the nematic phase of the inventive media extends over the same preferred ranges as in the previous (i.e. the fourth preferred embodiment).

Component A preferably is used in a concentration from 1% to 65%, more preferably from 2% to 60%, more preferably from 3% to 50%, and most preferably from 5% to 40% of the total mixture.

Component B preferably is used in a concentration from 5% to 60%, more preferably from 10% to 55%, more preferably from 15% to 50% and most preferably from 20% to 45% of the total mixture.

Component C preferably is used in a concentration from 0% to 70%, more preferably from 10% to 60%, more preferably from 20% to 50% and most preferably from 15% to 50% of the total mixture.

Component D preferably is used in a concentration from 0% to 50%, preferably from 1% to 40%, more preferably from 5% to 30% and most preferably from 10% to 20% of the total mixture.

Component E preferably is used in a concentration from 0% to 30%, preferably from 0% to 15% and most preferably from 1% to 10% of the total mixture.

Optionally, the inventive media can comprise further liquid crystal compounds in order to adjust the physical properties. Such compounds are known to the expert. Their concentration in the media according to the instant invention is preferably 0% to 30%, more preferably 0.1% to 20% and most preferably 1% to 15%.

In the first preferred embodiment of the present invention mentioned above component A preferably is used in a concentration from 40% to 65%, more preferably from 45% to 60% and most preferably from 50% to 57% of the total mixture, whereas component D preferably is used in a concentration from 5% to 40%, preferably from 10% to 35% and most preferably from 10% to 30% of the total mixture.

In this preferred embodiment the media preferably comprise one or more compounds of formula VI and most preferably of formula VI-2.

Especially in the second preferred embodiment of the present invention mentioned above component C preferably comprises one or more compounds of formula IV, more preferably of formula IV-1, more preferably of formula CC-n-V and/or CC-n-Vm, more preferably of formula CC-n-V1 and/or CC-n-V and most preferably selected from the group of formulae CC-3-V, CC-4-V, CC-5-V and CC-3-V1.

Preferably, the liquid crystal media contain 50% to 100%, more preferably 70% to 100% and most preferably 80% to 100% and in particular 90% to 100% totally of components A, B, C and D, preferably of components A, B and C, which, in turn, contain, preferably predominantly consist of, more preferably essentially consist of, and most preferably entirely consist of one or more of compounds of formulae I, II, III, IV, V, VI and VII, preferably of formulae I, II, III, IV, V and VI, respectively.

In the present application the term dielectrically positive means compounds or components with Δ∈>3.0, dielectrically neutral with −1.5≦Δ∈≦3.0 and dielectrically negative with Δ∈<−1.5. Δ∈ is determined at a frequency of 1 kHz and at 20° C. The dielectric anisotropy of the respective compound is determined from the results of a solution of 10% of the respective individual compound in a nematic host mixture. In case the solubility of the respective compound in the host mixture is less than 10% the concentration is reduced to 5%. The capacities of the test mixtures are determined both in a cell with homeotropic and with homogeneous alignment. The cell gap of both types of cells is approximately 20 μm. The voltage applied is a rectangular wave with a frequency of 1 kHz and a root mean square value typically of 0.5 V to 1.0 V, however, it is always selected to be below the capacitive threshold of the respective test mixture.

For dielectrically positive compounds the mixture ZLI-4792 and for dielectrically neutral, as well as for dielectrically negative compounds, the mixture ZLI-3086, both of Merck KGaA, Germany are used as host mixture, respectively. The dielectric permittivities of the compounds are determined from the change of the respective values of the host mixture upon addition of the compounds of interest. The values are extrapolated to a concentration of the compounds of interest of 100%.

Components having a nematic phase at the measurement temperature of 20° C. are measured as such, all others are treated like compounds.

The term threshold voltage refers in the instant application to the optical threshold and is given for 10% relative contrast (V₁₀) and the term saturation voltage refers to the optical saturation and is given for 90% relative contrast (V₉₀) both, if not explicitly stated otherwise. The capacitive threshold voltage (V₀), also called Freedericksz-threshold (V_(Fr)) is only used if explicitly mentioned.

The ranges of parameters given in this application are all including the limiting values, unless explicitly stated otherwise.

Throughout this application, unless explicitly stated otherwise, all concentrations are given in mass percent and relate to the respective complete mixture, all temperatures are given in degrees centigrade (Celsius) and all differences of temperatures in degrees centigrade. All physical properties have been and are determined according to “Merck Liquid Crystals, Physical Properties of Liquid Crystals”, Status November 1997, Merck KGaA, Germany and are given for a temperature of 20° C., unless explicitly stated otherwise. The optical anisotropy (Δn) is determined at a wavelength of 589.3 nm. The dielectric anisotropy (Δ∈) is determined at a frequency of 1 kHz. The threshold voltages, as well as all other electro-optical properties have been determined with test cells prepared at Merck KGaA, Germany. The test cells for the determination of Δ∈ had a cell gap of approximately 20 μm. The electrode was a circular ITO electrode with an area of 1.13 cm² and a guard ring. The orientation layers were lecithin for homeotropic orientation (∈_(∥)) and polyimide AL-1054 from Japan Synthetic Rubber for homogeneous orientation (∈_(⊥)). The capacities were determined with a frequency response analyser Solatron 1260 using a sine wave with a voltage of 0.3 V_(rms). The light used in the electro-optical measurements was white light. The set up used was commercially available equipment of Otsuka, Japan. The characteristic voltages have been determined under perpendicular observation. The threshold (V₁₀)—mid grey (V₅₀)—and saturation (V₉₀) voltages have been determined for 10%, 50% and 90% relative contrast, respectively.

The liquid crystal media according to the present invention can contain further additives and chiral dopants in usual concentrations. The total concentration of these further constituents is in the range of 0% to 10%, preferably 0.1% to 6%, based on the total mixture. The concentrations of the individual compounds used each are preferably in the range of 0.1% to 3%. The concentration of these and of similar additives is not taken into consideration for the values and ranges of the concentrations of the liquid crystal components and compounds of the liquid crystal media in this application.

The inventive liquid crystal media according to the present invention consist of several compounds, preferably of 3 to 30, more preferably of 4 to 20 and most preferably of 4 to 16 compounds. These compounds are mixed in conventional way. As a rule, the required amount of the compound used in the smaller amount is dissolved in the compound used in the greater amount. In case the temperature is above the clearing point of the compound used in the higher concentration, it is particularly easy to observe completion of the process of dissolution. It is, however, also possible to prepare the media by other conventional ways, e.g. using so called pre-mixtures, which can be, e.g., homologous or eutectic mixtures of compounds or using so called multi-bottle-systems, the constituents of which are ready to use mixtures themselves.

By addition of suitable additives, the liquid crystal media according to the instant invention can be modified in such a way, that they are usable in all known types of liquid crystal displays, either using the liquid crystal media as such, like TN-, TN-AMD, ECB-AMD, VAN-AMD, IPS and OCB LCDs and in particular in composite systems, like PDLC, NCAP, PN LCDs and especially in ASM-PA LCDs.

The melting point T(C,N), the transition from the smectic (S) to the nematic (N) phase T(S,N) and the clearing point T(N,I) of the liquid crystals are given in degrees centigrade.

In the present application and especially in the following examples, the structures of the liquid crystal compounds are represented by abbreviations also called acronyms. The transformation of the abbreviations into the corresponding structures is straight forward according to the following two tables A and B. All groups C_(n)H_(2n+1) and C_(m)H_(2m+1) are straight chain alkyl groups with n respectively m C-atoms. The interpretation of table B is self-evident. Table A does only list the abbreviations for the cores of the structures. The individual compounds are denoted by the abbreviation of the core followed by a hyphen and a code specifying the substituents R¹, R², L¹ and L² follows:

Code for R¹, R², L¹, L² R¹ R² L¹ L² nm C_(n)H_(2n+1) C_(m)H_(2m+1) H H nOm C_(n)H_(2n+1) OC_(m)H_(2m+1) H H nO•m OC_(n)H_(2n+1) C_(m)H_(2m+1) H H n C_(n)H_(2n+1) CN H H nN•F C_(n)H_(2n+1) CN H F nN•F•F C_(n)H_(2n+1) CN F F nF C_(n)H_(2n+1) F H H nF•F C_(n)H_(2n+1) F H F nF•F•F C_(n)H_(2n+1) F F F nOF OC_(n)H_(2n+1) F H H nCl C_(n)H_(2n+1) Cl H H nCl•F C_(n)H_(2n+1) Cl H F nCl•F•F C_(n)H_(2n+1) Cl F F nCF₃ C_(n)H_(2n+1) CF₃ H H nCF₃•F C_(n)H_(2n+1) CF₃ H F nCF₃•F•F C_(n)H_(2n+1) CF₃ F F nOCF₃ C_(n)H_(2n+1) OCF₃ H H nOCF₃•F C_(n)H_(2n+1) OCF₃ H F nOCF₃•F•F C_(n)H_(2n+1) OCF₃ F F nOCF₂ C_(n)H_(2n+1) OCHF₂ H H nOCF₂•F C_(n)H_(2n+1) OCHF₂ H F nOCF₂•F•F C_(n)H_(2n+1) OCHF₂ F F nS C_(n)H_(2n+1) NCS H H nS•F C_(n)H_(2n+1) NCS H F nS•F•F C_(n)H_(2n+1) NCS F F rVsN C_(r)H_(2r+1)—CH═CH—C_(s)H_(2s)— CN H H rEsN C_(r)H_(2r+1)—O—C_(s)H_(2s)— CN H H nAm C_(n)H_(2n+1) COOC_(m)H_(2m+1) H H

TABLE A

TABLE B

The liquid crystal media according to the instant invention contain preferably

-   -   seven or more, preferably eight or more compounds, preferably of         different formulae, selected from the group of compounds of         tables A and B and/or     -   one or more, more preferably two or more, preferably three or         more compounds, preferably of different formulae, selected from         the group of compounds of table A and/or     -   three or more, more preferably four or more compounds, more         preferably five or more compounds, preferably of different         formulae, selected from the group of compounds of table B.

In the foregoing and in the following examples, all temperatures are set forth uncorrected in degrees Celsius; and, unless otherwise indicated, all parts and percentages are by weight.

The entire disclosures of all applications, patents and publications, cited above and below, including European Patent Application No. 06024514.9, filed Nov. 27, 2006, are hereby incorporated by reference.

EXAMPLES

The examples given in the following are illustrating the present invention without limiting it in any way.

However, the physical properties compositions illustrate to the expert, which properties can be achieved and in which ranges they can be modified. Especially the combination of the various properties, which can be preferably achieved, is thus well defined for the expert.

Example 1

A liquid crystal mixture is realized with the composition and properties given in the following table.

Composition Compound No. Abbreviation Conc./% 1 ADCQU-3-F 8.0 2 CCZU-3-F 5.0 3 PGU-2-F 3.0 4 PUQU-3-F 19.0 5 CC-3-V1 10.0 6 CC-3-V 42.0 7 CCP-V-1 9.0 8 CCP-V2-1 4.0 Σ 100.00 Physical Properties T(N, I) = 68° C. n_(e) (20° C., 589.3 nm) = 1.5608 Δn (20° C., 589.3 nm) = 0.0824 ε|| (20° C., 1 kHz) = 10.6 Δε (20° C., 1 kHz) = 7.3 γ₁ (20° C.) = 51 mPa · s k₁ (20° C.) = 11.6 pN k₃/k₁ (20° C.) = 1.13 V₀ (20° C.) = 1.32 V

This mixture has a favourably low value of Δn, a moderately high value of Δ∈ and a very low rotational viscosity. Thus it is very well suited for displays operating in the IPS mode.

Example 2

A liquid crystal mixture is realized with the composition and properties given in the following table.

Composition Compound No. Abbreviation Conc./% 1 ADCQU-2-F 8.0 2 CCZU-3-F 5.0 3 PGU-2-F 2.5 4 PUQU-3-F 19.0 5 CC-3-V1 10.0 6 CC-3-V 40.5 7 CCP-V-1 10.0 8 CCP-V2-1 5.0 Σ 100.00 Physical Properties T(N, I) = 69.5° C. n_(e) (20° C., 589.3 nm) = 1.5605 Δn (20° C., 589.3 nm) = 0.0820 ε|| (20° C., 1 kHz) = 10.7 Δε (20° C., 1 kHz) = 7.4 γ₁ (20° C.) = 52 mPa · s

This mixture has a rather low value of Δn, a rather high value of Δ∈ and a low rotational viscosity. Thus it is very well suited for displays operating in the IPS mode.

Example 3

A liquid crystal mixture is realized with the composition and properties given in the following table.

Composition Compound No. Abbreviation Conc./% 1 ADCQU-2-F 4.0 2 ADCQU-3-F 4.0 3 CCZU-3-F 5.5 4 PGU-2-F 2.5 5 PUQU-3-F 19.0 6 CC-3-V1 10.0 7 CC-3-V 41.0 8 CCP-V-1 9.0 9 CCP-V2-1 5.0 Σ 100.00 Physical Properties T(N, I) = 69.5° C. n_(e) (20° C., 589.3 nm) = 1.5601 Δn (20° C., 589.3 nm) = 0.0820 ε|| (20° C., 1 kHz) = 10.7 Δε (20° C., 1 kHz) = 7.4 γ₁ (20° C.) = 52 mPa · s

This mixture has a favourably low value of Δn, a high value of Δ∈ and a rather low rotational viscosity. Thus it is very well suited for displays operating in the IPS mode.

The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples.

While the invention has been illustrated with respect to the production and of particular compounds, it is apparent that variations and modifications of the invention can be made without departing from the spirit or scope of the invention. 

1. A liquid crystal medium comprising: a first dielectrically positive component, component A, comprising one or more dielectrically positive compounds of formula I

wherein R¹ is alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms,

 are independently of each other

X¹ is halogen, halogenated alkyl having 1 to 3 C-atoms, alkoxy having 1 to 3 C-atoms, halogenated alkenyl having 2 to 3 C-atoms, or alkenyloxy having 2 or 3 C-atoms; and a second dielectrically positive component, component B, comprising one or more dielectrically positive compounds, selected from compounds of formulae II and III

wherein R² and R³, independently of each other, are alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms,

 are, independently of each other,

L²¹, L²², L³¹ and L³², are, independently of each other, H or F, X² and X³ are, independently of each other, halogen, halogenated alkyl having 1 to 3 C-atoms, alkoxy having 1 to 3 C-atoms, halogenated alkenyl having 2 to 3 C-atoms, or alkenyloxy having 2 or 3 C-atoms, Z³ is —CH₂CH₂—, —CF₂CF₂—, —COO—, trans- —CH═CH—, trans- —CF═CF—, —CH₂O— or a single bond, and l, m, n and o are, independently of each other, 0 or 1, and from which compounds of formula I are excluded; and optionally a dielectrically neutral component, component C, comprising one or more dielectrically neutral compounds of formula IV

wherein R⁴¹, and R⁴², independently of each other, are alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms,

 independently of each other, and in case

 is present twice, also these, independently of each other, are

Z⁴¹ and Z⁴² are, independently of each other, and in case Z⁴¹ is present twice, also these independently of each other, —CH₂CH₂—, —COO—, trans- —CH═CH—, trans- —CF═CF—, —CH₂O—, —CF₂O—, —C≡C— or a single bond, and p is 0, 1 or
 2. 2. A liquid crystal medium according to claim 1, wherein the concentration of component A in the medium is 1% to 70%.
 3. A liquid crystal medium according to claim 1, wherein component A comprises one or more compounds selected from formulae I-1 to I-3

wherein R¹ is alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms, X¹ is halogen, halogenated alkyl having 1 to 3 C-atoms, alkoxy having 1 to 3 C-atoms, halogenated alkenyl having 2 to 3 C-atoms, or alkenyloxy having 2 or 3 C-atoms.
 4. A liquid crystal medium according to claim 1, wherein Component B comprises one or more compounds of formula II.
 5. A liquid crystal medium according to claim 4, wherein component B, comprises one or more dielectrically positive compounds having a dielectric anisotropy of more than 3, selected from compounds of formulae II-1 and II-2

wherein L²³ and L²⁴ are, independently of each other and of the other parameters, H or F.
 6. A liquid crystal medium according to claim 1, wherein Component B comprises one or more compounds of formula III.
 7. A liquid crystal medium according to claim 6, wherein component B, comprises one or more dielectrically positive compounds having a dielectric anisotropy of more than 3, selected from formulae III-1 and III-2


8. A liquid crystal medium according to claim 1, wherein said medium contains Component C which comprises one or more dielectrically neutral compounds of formula IV.
 9. A liquid crystal medium according to claim 8, wherein Component C comprises one or more compounds selected from formulae IV-1 to IV-5


10. A liquid crystal medium according to claim 1, wherein said medium further comprises one or more dielectrically positive compounds of formula V

wherein R⁵ is alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms,

 are, independently of each other,

L⁵¹ and L⁵², are, independently of each other, H or F, X⁵ is halogen, halogenated alkyl having 1 to 3 C-atoms, alkoxy having 1 to 3 C-atoms, halogenated alkenyl having 2 to 3 C-atoms, or alkenyloxy having 2 or 3 C-atoms, Z⁵ is —CH₂CH₂—, —CF₂CF₂—, —COO—, trans- —CH═CH—, trans- —CF═CF— or —CH₂O, and q is 0 or
 1. 11. A liquid crystal medium according to claim 1, wherein said medium further comprises a component D which comprises one or more compounds of formula VI

wherein R⁶¹ and R⁶², independently of each other, are alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms,

 and in case it is occurring twice in each occurrence independently of each other, is

Z⁶¹ and Z⁶² are, independently of each other, and in case Z⁶¹ is present twice, also these independently of each other, —CH₂CH₂—, —COO—, trans- —CH═CH—, trans- —CF═CF—, —CH₂O—, —CF₂O, —C≡C— or a single bond, and r is 0, 1 or
 2. 12. A liquid crystal medium according to claim 1, wherein said medium further comprises component E, which has a negative dielectric anisotropy, and which comprises one or more dielectrically negative compounds of formula VII

wherein R⁷¹ and R⁷² independently of each other, are alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms,

Z⁷¹ and Z⁷² are, independently of each other, —CH₂CH₂—, —COO—, trans- CH═CH—, trans- —CF═CF—, —CH₂O—, —CF₂O— or a single bond, L⁷¹ and L⁷² are, independently of each other, C—F or N, and k is 0 or
 1. 13. A liquid crystal medium according to claim 1 wherein the concentration of the component A in said medium is the 1 to 65 wt. %, the concentration of the component B in said medium is 5 to 60 wt. %, and the concentration of the component C in said medium is 0 to 70 wt. %, wherein said medium optionally further contains a component D at a concentration in said medium of 0 to 50 wt. %, and optionally further contains a component E at a concentration in said medium of 0 to 30 wt. %, component D comprises one or more compounds of formula VI

wherein R⁶¹ and R⁶², independently of each other, are alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms,

 and in case it is occurring twice in each occurrence independently of each other, is

Z⁶¹ and Z⁶² are, independently of each other, and in case Z⁶¹ is present twice, also these independently of each other, —CH₂CH₂—, —COO—, trans- —CH═CH—, trans- —CF═CF—, —CH₂O—, —CF₂O—, —C≡C— or a single bond, and r is 0, 1 or 2, and component E, which has a negative dielectric anisotropy, comprises one or more dielectrically negative compounds of formula VII

wherein R⁷¹ and R⁷² independently of each other, are alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms,

Z⁷¹ and Z⁷² are, independently of each other, —CH₂CH₂—, —COO—, trans- CH═CH—, trans- —CF═CF—, —CH₂O—, —CF₂O— or a single bond, L⁷¹ and L⁷² are, independently of each other, C—F or N, and k is 0 or
 1. 14. A liquid crystal medium according to claim 11, wherein the concentration of the component A in said medium is the 2 to 60 wt. %, the concentration of the component B in said medium is 10 to 55 wt. %, the concentration of the component C in said medium is 10 to 60 wt. %, and the concentration of the component D in said medium is 1 to 40 wt. %, and wherein said medium optionally further contains a component E at a concentration in said medium of 0 to 15 wt %, and component E, which has a negative dielectric anisotropy, comprises one or more dielectrically negative compounds of formula VII

wherein R⁷¹ and R⁷² independently of each other, are alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms,

Z⁷¹ and Z⁷² are, independently of each other, —CH₂CH₂—, —COO—, trans- CH═CH—, trans- —CF═CF—, —CH₂O, —CF₂O— or a single bond, L⁷¹ and L⁷² are, independently of each other, C—F or N, and k is 0 or
 1. 15. A liquid crystal medium according to claim 12, wherein the concentration of the component A in said medium is the 3 to 50 wt. %, the concentration of the component B in said medium is 15 to 50 wt. %, the concentration of the component C in said medium is 20 to 50 wt. %, the concentration of the component D in said medium is 5 to 30 wt. %, and said medium further comprises a component E, which has a negative dielectric anisotropy, and which comprises one or more dielectrically negative compounds of formula VII

wherein R⁷¹ and R⁷² independently of each other, are alkyl having 1 to 7 C-atoms, alkoxy having 1 to 7 C-atoms, fluorinated alkyl having 1 to 7 C-atoms, fluorinated alkoxy having 1 to 7 C-atoms, alkenyl having 2 to 7 C-atoms, alkenyloxy having 2 to 7 C-atoms, alkoxyalkyl having 2 to 7 C-atoms, or fluorinated alkenyl having 2 to 7 C-atoms,

Z⁷¹ and Z⁷² are, independently of each other, —CH₂CH₂—, —COO—, trans- CH═CH—, trans- —CF═CF—, —CH₂O—, —CF₂O— or a single bond, L⁷¹ and L⁷² are, independently of each other, C—F or N, and k is 0 or 1, and wherein the concentration of component E in said medium is 1 to 10 wt. %.
 16. A liquid crystal medium according to claim 1, wherein said liquid crystal medium contains 50% to 100% of components A, B and C.
 17. A liquid crystal medium according to claim 11, wherein said liquid crystal medium contains 50% to 100% of components A, B, C, and D.
 18. A liquid crystal display comprising a liquid crystal medium according to claim
 1. 19. A liquid crystal display according to claim 18, wherein said display is addressed by an active matrix.
 20. A method of generating an electro-optical effect comprising applying a voltage to a liquid crystal display according to claim
 18. 21. A liquid crystal medium according to claim 4, wherein component B, comprises one or more compounds selected from compounds of formulae II-1a to II-1e


22. A liquid crystal medium according to claim 4, wherein component B, comprises one or more compounds selected from compounds of formulae II-2a to II-2d


23. A liquid crystal medium according to claim 6, wherein component B, comprises one or more compounds selected from compounds of formulae III-1a and III-1b

wherein the parameters L³³ and L³⁴ are, independently of each other and of the other parameters, H or F.
 24. A liquid crystal medium according to claim 6, wherein component B, comprises one or more compounds selected from compounds of formulae III-2a to III-2g


25. A liquid crystal medium according to claim 1, wherein said medium further comprises one or more compounds of formula III-3


26. A liquid crystal medium according to claim 1, wherein the Δn of said medium, at 589 nm (Na^(D)) and 20° C., is in the range of 0.060 to 0.135.
 27. A liquid crystal medium according to claim 1, wherein the Δ∈ of said medium, at 1 kHz and 20° C., is 4.0 or more.
 28. A liquid crystal medium according to claim 1, wherein the Δn of said medium is in the range of 0.090 to 0.125, and the Δ∈ is in the range from 4.0 to 10.0.
 29. A liquid crystal medium according to claim 1, wherein the Δn of said medium, is in the range of 0.085 to 0.130, and the Δ∈ is 6.0 or more. 